9 February 2012
New coating promises to turn an atomic force microscope into an even more useful tool.
IBM’s Zurich Research Laboratory—where several groundbreaking microscopy tools have been invented—has created a tough new coating for the tip of an atomic force microscope (AFM), a device that can be used to capture nanoscale imagery as the tip is run over a surface on the end of a microscopic cantilever. The coating could expand the range of ways that AFM can be used to include making lithographic masks for electronic manufacturing with features 10 nanometers in size—beyond the limits of traditional processes such as e-beam lithography.
Scientists have long wanted to use atomic tips in such ways, but it’s difficult to prevent the silicon tips from wearing down too quickly as they move across a surface, says Mark Lantz, manager of storage research at IBM’s Zurich Research Laboratory.
A common way to make atomic tips more wear-resistant is to add a diamond coating. But diamond is surprisingly unstable, says Lantz. It will burn when heated to around 400 °C, which is impractical for certain uses. IBM had originally set its sights on using heated arrays of tips to burn pits in thin polymer substrates as a way of storing digital memory—a concept known asmillipede memory. IBM is no longer pursuing millipede memory as a consumer technology, although it hopes to adapt it for archival storage systems or high-speed biological imaging of subcellular processes.
The IBM researchers apply a layer of silicon carbide, a material that is slightly softer than diamond but does not burn when heated. “Silicon carbide has an extremely high melting temperature, so even at 1,400 °C, it still maintains its strength,” says Lantz.
The process involves implanting carbon ions in a tip by surrounding the tip with plasma containing the carbon ions, then applying a high voltage between the plasma and the tip, causing the ions to become embedded in its surface. Next, the tip is heated to 1,100 °C, a temperature sufficient to make the carbon ions react with nearby silicon atoms to form a thin coating of silicon carbide. “The coating thickness is about 15 to 18 nanometers, and at the very apex of the tip, where the dimensions become less than this, the last 30 nanometers of the tip, is just pure silicon carbide,” says Lantz.
Chad Mirkin, director of the International Institute for Nanotechnology, at Northwestern University, says that in general, and for tasks such as memory storage, “the biggest issue that limits utility is speed.” But he adds that using an AFM to make a lithographic mask would make sense, since speed is not as important.